Product Description:
PC+ABS, excellent flow/impact/high heat resistance. Low temperature ductility.
Material Status |
|
UL Yellow Card 1 |
|
Search for UL Yellow Card |
|
Availability | Latin AmericaNorth America |
Features | DuctileGood FlowGood Impact ResistanceHigh Heat Resistance |
Uses | Additive Manufacturing (3D Printing)AppliancesAutomotive ApplicationsAutomotive Exterior PartsAutomotive Interior PartsAutomotive LightingAutomotive Under the HoodAutomotive Window EncapsulationConstruction ApplicationsElectrical/Electronic ApplicationsElectronic DisplaysFluid HandlingHousehold GoodsIndustrial ApplicationsLawn and Garden EquipmentLensesLighting ApplicationsMedical/Healthcare ApplicationsNon-specific Food ApplicationsOutdoor ApplicationsPharmaceuticalsRail ApplicationsSporting Goods |
Processing Method |
|
Multi-Point Data |
|
Also Available In | Asia PacificEurope |
| Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | 1.15 | g/cm3 | ASTM D792 |
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 19 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 24 | cm3/10min | ISO 1133 |
Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 2 | 2270 | MPa | ASTM D638 |
-- | 2400 | MPa | ISO 527-2/1 |
Tensile Strength | |||
Yield 3 | 57.0 | MPa | ASTM D638 |
Yield | 55.0 | MPa | ISO 527-2/50 |
Tensile Elongation | |||
Yield 3 | 5.0 | % | ASTM D638 |
Yield | 4.8 | % | ISO 527-2/50 |
Break 3 | 150 | % | ASTM D638 |
Break | 110 | % | ISO 527-2/50 |
Flexural Modulus | |||
50.0 mm Span 4 | 2340 | MPa | ASTM D790 |
-- | 2250 | MPa | ISO 178 |
Flexural Stress | |||
-- | 86.0 | MPa | ISO 178 |
Yield, 50.0 mm Span 4 | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact | |||
-30°C | 480 | J/m | ASTM D256 |
23°C | 590 | J/m | ASTM D256 |
-30°C 5 | 34 | kJ/m2 | ISO 180/1A |
23°C 5 | 49 | kJ/m2 | ISO 180/1A |
Instrumented Dart Impact | ASTM D3763 | ||
-30°C, Total Energy | 54.0 | J | |
23°C, Total Energy | 54.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed, 3.20 mm | 129 | °C | ASTM D648 |
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | 130 | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed, 3.20 mm | 112 | °C | ASTM D648 |
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | 110 | °C | ISO 75-2/Af |
Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
CLTE - Flow (-40 to 40°C) | 7.2E-5 | cm/cm/°C | ASTM E831 |
RTI Elec | 105 | °C | UL 746 |
RTI Imp | 80.0 | °C | UL 746 |
RTI Str | 105 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
High Amp Arc Ignition (HAI) 7 | PLC 1 | UL 746 | |
Hot-wire Ignition (HWI) | PLC 3 | UL 746 | |
| Flammability | Nominal Value | Test Method | |
Flame Rating (1.2 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
Drying Temperature | 100 to 110 | °C | |
Drying Time | 3.0 to 4.0 | hr | |
Suggested Max Moisture | 0.020 | % | |
Suggested Shot Size | 30 to 80 | % | |
Hopper Temperature | 60 to 80 | °C | |
Rear Temperature | 250 to 290 | °C | |
Middle Temperature | 255 to 295 | °C | |
Front Temperature | 260 to 300 | °C | |
Nozzle Temperature | 275 to 300 | °C | |
Processing (Melt) Temp | 275 to 300 | °C | |
Mold Temperature | 60 to 90 | °C | |
Back Pressure | 0.300 to 0.700 | MPa | |
Screw Speed | 40 to 70 | rpm | |
Vent Depth | 0.038 to 0.076 | mm | |
| Injection Notes | |||
Injection Molding Parameters
| |||