科思创 PC 2865 物性表
Makrolon® 2865
Polycarbonate
Covestro - Polycarbonates
Product Description:
MVR (300°C/1.2 kg) 10 cm3/10 min; flame retardant; UL 94V-2/1.5 mm and 3.0 mm; medium viscosity; easy release; injection molding - melt temperature 280 - 320°C; available in transparent, translucent and opaque colors
| General | |
Material Status |
|
Literature 1 |
|
UL Yellow Card 2 |
|
Search for UL Yellow Card |
|
Availability | Africa & Middle EastAsia PacificEuropeLatin AmericaNorth America |
Additive |
|
Features | Flame RetardantGood Mold ReleaseMedium Viscosity |
RoHS Compliance |
|
Appearance | Clear/TransparentColors AvailableOpaqueTranslucent |
Processing Method |
|
Multi-Point Data | Specific Volume vs Temperature (ISO 11403-2)Viscosity vs. Shear Rate (ISO 11403-2) |
| Physical | Nominal Value | Unit | Test Method |
Density (23°C) | 1.20 | g/cm3 | ISO 1183 |
Apparent (Bulk) Density 3 | 0.64 | g/cm3 | ISO 60 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 10 | cm3/10min | ISO 1133 |
Molding Shrinkage | |||
Across Flow | 0.60 to 0.80 | % | ISO 2577 |
Flow | 0.60 to 0.80 | % | ISO 2577 |
Across Flow : 280°C, 2.00 mm 4 | 0.70 | % | ISO 294-4 |
Flow : 2.00 mm 4 | 0.65 | % | ISO 294-4 |
Water Absorption | ISO 62 | ||
Saturation, 23°C | 0.30 | % | |
Equilibrium, 23°C, 50% RH | 0.12 | % | |
| Hardness | Nominal Value | Unit | Test Method |
Ball Indentation Hardness | 115 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/1 |
Tensile Stress | ISO 527-2/50 | ||
Yield, 23°C | 66.0 | MPa | |
Break, 23°C | 70.0 | MPa | |
Tensile Strain | ISO 527-2/50 | ||
Yield, 23°C | 6.2 | % | |
Break, 23°C | 130 | % | |
Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
Tensile Creep Modulus | ISO 899-1 | ||
1 hr | 2200 | MPa | |
1000 hr | 1900 | MPa | |
Flexural Modulus 5 (23°C) | 2400 | MPa | ISO 178 |
Flexural Stress 5 | ISO 178 | ||
23°C | 97.0 | MPa | |
3.5% Strain, 23°C | 73.0 | MPa | |
Flexural Strain at Flexural Strength 6 (23°C) | 7.1 | % | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
Water Vapor Transmission Rate (23°C, 85% RH, 100 μm) | 15 | g/m2/24 hr | ISO 15106-1 |
Carbon Dioxide Permeability (23°C, 25.4 μm) | 16900 | cm3/m2/bar/24 hr | ISO 2556 |
Gas Permeation | ISO 2556 | ||
Carbon Dioxide : 100.0 μm | 3800 | cm3/m2/bar/24 hr | |
Nitrogen : 25.4 μm | 510 | cm3/m2/bar/24 hr | |
Nitrogen : 100.0 μm | 120 | cm3/m2/bar/24 hr | |
Oxygen : 25.4 μm | 2760 | cm3/m2/bar/24 hr | |
Oxygen : 100.0 μm | 650 | cm3/m2/bar/24 hr | |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength 7 | ISO 179/1eA | ||
-30°C, Complete Break | 16 | kJ/m2 | |
23°C, Partial Break | 75 | kJ/m2 | |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-60°C | No Break | ||
-30°C | No Break | ||
23°C | No Break | ||
Notched Izod Impact Strength 7 | ISO 180/A | ||
-30°C, Complete Break | 12 | kJ/m2 | |
23°C, Partial Break | 65 | kJ/m2 | |
Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
-30°C | 65.0 | J | |
23°C | 60.0 | J | |
Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
-30°C | 6300 | N | |
23°C | 5400 | N |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 137 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
Glass Transition Temperature 8 | 145 | °C | ISO 11357-2 |
科思创PC塑料是一种无定形、无嗅、无味、无毒而透明的热塑性聚合物，是一具有良好透明性的塑料品种，具有较好的机械强度、耐热性能、耐紫外辐射及耐电综合性能，耐冲击强度高，蠕变性小，制品尺寸稳定，易增强，无毒卫生，能着色，具有良好的性价比和可化学修饰物理改性潜力，是综合性能优异、用途极为广泛的重要工程塑料品种。1954年德国拜耳公司首先研制开发成功，并于1958年实现了工业化。PC的特定结构决定了其特有的优良性质。主链中大共轭苯环使大分子变得较为柔顺，同时使它在有机溶剂中的溶解性和吸水性降低；极性羰基增大了分子问作用力，使分子链的刚性增加；氧基则使PC分子链兼具柔性和韧性；易溶于某些有机极性溶剂，同时电绝缘性稍差于非极性和弱极性聚合物则是由于酯基的存在。在暂不考虑R基的情况下，由于苯环和羰基的作用较氧基强烈，故总体来说，PC分子链的刚性较大，玻璃化温度高，抗冲击性能好。同时，分子链的刚性和分子间的作用力增大了位阻，使PC的机械强度增高。
科思创PC塑料按功能特性可分为通用级PC、透明级PC、医药食品级PC、阻燃PC、耐热PC、耐候PC、润滑PC、玻璃纤维增强PC、碳纤维增强PC、无机物填充PC、电磁屏蔽PC、抗静电PC等，以及复合级PC。各品种又可按树脂熔体指数或混配改性添加剂成分不同，细分为更多的具体牌号。聚碳酸酯PC可采用共聚或共混方法改性，产生出许多具有特殊优良性能的品种，这在很大程度上拓宽了聚碳酸酯PC的品种和应用领域。聚碳酸酯PC系优良的电绝缘材料。在宽广的温度和温度范围内具有良好且稳定的电绝缘性。它还具有耐热性、耐寒性、阻燃性、低烟性及低的腐蚀气体排放性、尺寸稳定性，而且具有极高的冲击强度，特别适用于制造办公机器、家用电器、通信设备、电工器械和仪器仪表等，已广泛用于计算机、便携式计算机、打印机、复印机、录像机、彩色电视机、冰箱、吸尘器、电话、移动电话、手机、电动工具、实验室分析仪器和食品加工机械等，PC可用作诸如外壳、机体、支架、冰箱冷冻室抽屉、高精度重要零部件、透明的电器仪表屏、灯具、开关、计算机配件、高清晰度大型电视屏幕、液晶平面显示器（导光板、扩散板及光学薄膜等）。
科思创PC塑料是高分子化合物，PC胶料是当今五大工程塑料之一，PC是一种综合性能优良的热塑性工程塑料。可用于制造机械、汽车和精密仪器等零部件，可制成精度很高的成型品，也可用于电子元件和电动工具部件。但PC的加工成型要求较高，本身无自润滑性，不适合制造带金属嵌件的制品。由于PC本身无毒，耐化学品性好，食品卫生性能优良，可以广泛地应用日常生活中。特别是它的透明性能优异于其他工程塑料，所以广泛应用于航空玻璃、灯具、安全玻璃、办公设备、激光光盘等领域。可以说在国民经济的各个领域，PC都获得了广泛的应用，而且还在不断扩大。工程塑料PC以其优秀的综合性能。PC具有优异的电绝缘性、延伸性、透明性、尺寸稳定性、高抗冲强度及耐化学腐蚀性，较高的耐热性和耐寒性。PC被广泛用于汽车、电子电气、建筑材料、机械零件、办公自动化设备、包装业、运动器械、医疗保健、光盘和家庭用品等领域。
科思创PC-现代汽车制造追求安全、环保、节能、轻型和美观等要求。用聚碳酸酯PC制成的汽车零部件具有重量轻、抗冲击、韧性好、成本低、造型美观、节约能源和保持环境等优点。聚碳酸酯PC透明、耐热、抗冲击和易成型，适用于制汽车头灯。现代汽车头灯造型美观、形状复杂多样、有很高的弯曲率，这些因素使得传统玻璃头灯的制造陷入困境。而聚碳酸酯PC易成型加工，可将车灯头部、连接片和灯体等全部模塑在透镜中，制造出美观、形状复杂的头灯。高耐热聚碳酸酯在生产聚光镜和反射镜部件时可直接进行真空喷镀金属。在真空喷镀时，温度高达到 200℃。此时，PC产品表面不鼓起、不出现雾斑、不剥离。由于采用了聚碳酸酯PC，前车灯罩重量较无机玻璃减轻了0.5-1.4kg。目前，尼桑、福特、奔 驰、沃尔沃等 车型均已采用光学聚碳酸酯作汽车灯罩材料
。