Crastin S600F10 NC010塑胶原料
Literature 1 |
|
UL Yellow Card 2 |
|
Search for UL Yellow Card |
|
Availability | Africa & Middle EastAsia PacificEuropeLatin AmericaNorth America |
Additive |
|
Features |
|
RoHS Compliance |
|
Forms |
|
Processing Method | CoatingExtrusionInjection Molding |
Multi-Point Data |
|
Part Marking Code (ISO 11469) |
|
Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
Density | 1.30 | g/cm3 | ISO 1183 |
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 10 | cm3/10min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 1.7 | % | |
Flow | 1.7 | % | |
Water Absorption | ISO 62 | ||
Saturation, 23°C, 2.00 mm | 0.50 | % | |
Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % | |
Intrinsic Viscosity | 1.2 | ISO 307, 1157, 1628 | |
| Hardness | Nominal Value | Unit | Test Method |
Ball Indentation Hardness (H 358/30) | 139 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 2600 | MPa | ISO 527-2 |
Tensile Stress (Yield) | 57.0 | MPa | ISO 527-2 |
Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
Tensile Creep Modulus | ISO 899-1 | ||
1 hr | 2300 | MPa | |
1000 hr | 1800 | MPa | |
Flexural Modulus | 2400 | MPa | ISO 178 |
Flexural Stress | 84.0 | MPa | ISO 178 |
Poisson's Ratio | 0.38 | ||
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | ||
-30°C | 4.0 | kJ/m2 | |
23°C | 5.0 | kJ/m2 | |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-30°C | No Break | ||
23°C | No Break |