Crastin SK652FR NC010塑胶原料
Availability | Africa & Middle EastAsia PacificEuropeLatin AmericaNorth America |
Filler / Reinforcement |
|
RoHS Compliance |
|
Processing Method | ExtrusionInjection Molding |
Multi-Point Data |
|
Part Marking Code (ISO 11469) |
|
Resin ID (ISO 1043) |
| Physical | Nominal Value | Unit | Test Method |
Density | 1.53 | g/cm3 | ISO 1183 |
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 7.0 | cm3/10min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 1.1 | % | |
Across Flow : 80°C, 48 hr | 0.20 | % | |
Flow | 0.30 | % | |
Flow : 80°C, 48 hr | 0.10 | % | |
Water Absorption | ISO 62 | ||
Saturation, 23°C, 2.00 mm | 0.35 | % | |
Equilibrium, 23°C, 2.00 mm, 50% RH | 0.15 | % | |
| Hardness | Nominal Value | Unit | Test Method |
Ball Indentation Hardness (H 358/30) | 205 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 10000 | MPa | ISO 527-2 |
Tensile Stress (Break) | 140 | MPa | ISO 527-2 |
Tensile Strain (Break) | 2.7 | % | ISO 527-2 |
Flexural Modulus | 9000 | MPa | ISO 178 |
Flexural Stress | 200 | MPa | ISO 178 |
Poisson's Ratio | 0.34 | ||
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 10 | kJ/m2 | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | 65 | kJ/m2 | ISO 179/1eU |
Notched Izod Impact Strength (23°C) | 9.0 | kJ/m2 | ISO 180/1A |
Unnotched Izod Impact Strength | ISO 180/1U | ||
-40°C | 55 | kJ/m2 | |
-30°C | 55 | kJ/m2 | |
23°C | 60 | kJ/m2 |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
Ball Pressure Test (210°C) | Pass | IEC 60695-10-2 | |
Melting Temperature 3 | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
Burning Rate 4 (1.00 mm) | 54 | mm/min | ISO 3795 |
Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
0.75 mm | HB | ||
1.5 mm | HB | ||
Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
0.75 mm | 750 | °C | |
1.5 mm | 750 | °C | |
3.0 mm | 775 | °C | |
Oxygen Index | 20 | % | ISO 4589-2 |
FMVSS Flammability | B | FMVSS 302 |
| Fill Analysis | Nominal Value | Unit | Test Method |
Ejection Temperature | 170 | °C | |
Specific Heat Capacity of Melt | 1730 | J/kg/°C | |
Thermal Conductivity of Melt | 0.28 | W/m/K | |
| Additional Information | Nominal Value | Unit | Test Method |
Emission of Organic Compounds | 110 | μgC/g | VDA 277 |
Fogging - F-value (refraction) | 99 | % | ISO 6452 |
Odor | 3.00 | VDA 270 |
| Injection | Nominal Value | Unit |