Zytel® FE270050 BK099

CHARACTERISTICS

Regional availability

• Europe

• Near East/Africa

Processing

Injection Moulding

Delivery form

Pellets

Additives

Release agent

Special characteristics

Heat stabilised or stable to heat

PRODUCT TEXT

Common features of Zytel® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel® nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel® nylon resin, including most flame retardant grades, offer the ability to be coloured.

The good melt stability of Zytel® nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.

Zytel® nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.

Zytel® FE270050 is a 30% glass fibre reinforced polyamide 66 for gas and water injection moulding.

PRODUCT INFORMATION

DRY/COND.

TEST NORM

Resin Identification

PA66-(GF+MD)30

ISO 1043

Part Marking Code

>PA66-(GF+MD)30<

ISO 11469

ISO designation

ISO 16396-PA66,(GF+MD)30,M1CGHR,S14-090

-

MECHANICAL PROPERTIES

DRY/COND.

UNIT

TEST NORM

Tensile Modulus

9000/-

MPa

ISO 527-1/-2

Stress at break

160/-

MPa

ISO 527-1/-2

Strain at break

3/-

%

ISO 527-1/-2

Charpy impact strength, 23°C

60/-

kJ/m2

ISO 179/1eU

Charpy notched impact strength, 23°C

8/-

kJ/m2

ISO 179/1eA

Poisson's ratio

0.34/-

-

-

THERMAL PROPERTIES

DRY/COND.

UNIT

TEST NORM

Melting temperature, 10°C/min

262/*

°C

ISO 11357-1/-3

Glass transition temperature, 10°C/min

80/-

°C

ISO 11357-1/-2

Thermal conductivity of melt

0.21

W/(m K)

-

Eff. thermal diffusivity

6.85E-8

m2/s

-

Spec. heat capacity of melt

2290

J/(kg K)

-

FLAMMABILITY

DRY/COND.

UNIT

TEST NORM

Burning Behav. at 1.5mm nom. thickn.

HB/*

class

IEC 60695-11-10

Thickness tested

1.5/*

mm

IEC 60695-11-10

Burning Behav. at thickness h

HB/*

class

IEC 60695-11-10

Thickness tested

0.75/*

mm

IEC 60695-11-10

Oxygen index

24/*

%

ISO 4589-1/-2

FMVSS Class

B

-

ISO 3795 (FMVSS 302)

Burning rate, Thickness 1 mm

<80

mm/min

ISO 3795 (FMVSS 302)

OTHER PROPERTIES

DRY/COND.

UNIT

TEST NORM

Humidity absorption, 2mm

1.9/*

%

Sim. to ISO 62

Water absorption, 2mm

6/*

%

Sim. to ISO 62

Density

1370/-

kg/m3

ISO 1183

Density of melt

1200

kg/m3

-

INJECTION

DRY/COND.

UNIT

Drying Recommended

yes

Drying Temperature

80

°C

Drying Time, Dehumidified Dryer

2 - 4

h

Processing Moisture Content

≤0.2

%

Melt Temperature Optimum

295

°C

Min. melt temperature

285

°C

Max. melt temperature

305

°C

Max. screw tangential speed

0.2

m/s

Mold Temperature Optimum

100

°C

Min. mould temperature

70

°C

Max. mould temperature

120

°C

Hold pressure range

50 - 100

MPa

Hold pressure time

3

s/mm

Ejection temperature

210

°C