PRODUCT TEXT

Zytel® FG133F1 NC010 is unreinforced, nucleated polyamide 66. It has been developed for consideration into applications such as parts for the food industry.

FOOD CONTACT
This product is manufactured according to Good Manufacturing Practice (GMP) principles and generally accepted in food contact applications in Europe and the USA when meeting applicable use conditions. For details, individual compliance statements are available from your DuPont representative.

PRODUCT INFORMATION

DRY/COND.

TEST NORM

Resin Identification

PA66

ISO 1043

Part Marking Code

>PA66<

ISO 11469

ISO designation

ISO 16396-PA66,,M1G1NR,S14-040

-

RHEOLOGICAL PROPERTIES

DRY/COND.

UNIT

TEST NORM

Viscosity number

143/*

cm3/g

ISO 307, 1157, 1628

Moulding shrinkage, parallel

0.8/-

%

ISO 294-4, 2577

Moulding shrinkage, normal

1.0/-

%

ISO 294-4, 2577

MECHANICAL PROPERTIES

DRY/COND.

UNIT

TEST NORM

Tensile Modulus

3800/-

MPa

ISO 527-1/-2

Yield stress

94/-

MPa

ISO 527-1/-2

Yield strain

6/-

%

ISO 527-1/-2

Nominal strain at break

14/-

%

ISO 527-1/-2

Charpy notched impact strength, 23°C

3/-

kJ/m2

ISO 179/1eA

Poisson's ratio

0.36/-

-

-

THERMAL PROPERTIES

DRY/COND.

UNIT

TEST NORM

Melting temperature, 10°C/min

262/*

°C

ISO 11357-1/-3

Temp. of deflection under load, 1.8 MPa

78/*

°C

ISO 75-1/-2

FLAMMABILITY

DRY/COND.

UNIT

TEST NORM

FMVSS Class

B

-

ISO 3795 (FMVSS 302)

Burning rate, Thickness 1 mm

<80

mm/min

ISO 3795 (FMVSS 302)

OTHER PROPERTIES

DRY/COND.

UNIT

TEST NORM

Density

1140/-

kg/m3

ISO 1183

INJECTION

DRY/COND.

UNIT

Drying Recommended

yes

Drying Temperature

80

°C

Drying Time, Dehumidified Dryer

2 - 4

h

Processing Moisture Content

≤0.2

%

Melt Temperature Optimum

290

°C

Min. melt temperature

280

°C

Max. melt temperature

300

°C

Max. screw tangential speed

0.4

m/s

Mold Temperature Optimum

70

°C

Min. mould temperature

50

°C

Max. mould temperature

90

°C

Hold pressure range

50 - 100

MPa

Hold pressure time

4

s/mm

Ejection temperature

190

°C

EXTRUSION

DRY/COND.

UNIT

Drying Temperature

≤80

°C

Drying Time, Dehumidified Dryer

3 - 4

h

Processing Moisture Content

≤0.06

%

Melt Temperature Optimum

240

°C

Melt Temperature Range

235 - 250

°C