NYLON RESIN PA66Zytel® 132F NC010
CHARACTERISTICS
Regional availability
North America
Europe
Asia Pacific
South and Central America
Near East/Africa
Global
Processing
Injection Moulding
Delivery form
Pellets
Additives
Lubricants, Release agent
PRODUCT TEXT
Common features of Zytel® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel® nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel® nylon resin, including most flame retardant grades, offer the ability to be coloured.
The good melt stability of Zytel® nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.
Zytel® nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.
Zytel® 132F NC010 is a nucleated, lubricated polyamide 66 for injection moulding. It was developed for fast production cycles and high productivity applications.
DRY/COND.
TEST NORM
Resin Identification
PA66
ISO 1043
Part Marking Code
>PA66<
ISO 11469
ISO designation
ISO 16396-PA66,,M1G1NR,S14-030
-
DRY/COND.
UNIT
TEST NORM
Viscosity number
143/*
cm3/g
ISO 307, 1157, 1628
Moulding shrinkage, parallel
0.9/-
%
ISO 294-4, 2577
Moulding shrinkage, normal
1.2/-
%
ISO 294-4, 2577
DRY/COND.
UNIT
TEST NORM
Tensile Modulus
3400/1600
MPa
ISO 527-1/-2
Yield stress
91/60
MPa
ISO 527-1/-2
Yield strain
4.5/22
%
ISO 527-1/-2
Nominal strain at break
13/>50
%
ISO 527-1/-2
Strain at break, 50mm/min
20/-
%
ISO 527-1/-2
Flexural Modulus
3000/1400
MPa
ISO 178
Flexural Stress at 3.5%
100/-
MPa
ISO 178
Charpy impact strength, 23°C
300/N
kJ/m2
ISO 179/1eU
Charpy impact strength, -30°C
200/-
kJ/m2
ISO 179/1eU
Charpy notched impact strength, 23°C
4/8
kJ/m2
ISO 179/1eA
Charpy notched impact strength, -30°C
3.5/2.5
kJ/m2
ISO 179/1eA
Izod notched impact strength, 23°C
4/8
kJ/m2
ISO 180/1A
Izod notched impact strength, -30°C
4/2
kJ/m2
ISO 180/1A
Izod impact strength, 23°C
300/N
kJ/m2
ISO 180/1U
Poisson's ratio
0.37/0.42
-
-
DRY/COND.
UNIT
TEST NORM
Melting temperature, 10°C/min
262/*
°C
ISO 11357-1/-3
Glass transition temperature, 10°C/min
60/-
°C
ISO 11357-1/-2
Temp. of deflection under load, 1.8 MPa
75/*
°C
ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa
225/*
°C
ISO 75-1/-2
RTI, electrical, 0.75mm
130
°C
UL 746B
RTI, electrical, 1.5mm
130
°C
UL 746B
RTI, electrical, 3mm
130
°C
UL 746B
RTI, electrical, 6mm
130
°C
UL 746B
RTI, impact, 0.75mm
75
°C
UL 746B
RTI, impact, 1.5mm
75
°C
UL 746B
RTI, impact, 3mm
75
°C
UL 746B
RTI, impact, 6mm
75
°C
UL 746B
RTI, strength, 0.75mm
85
°C
UL 746B
RTI, strength, 1.5mm
85/*
°C
UL 746B
RTI, strength, 3mm
85
°C
UL 746B
RTI, strength, 6mm
85
°C
UL 746B