NYLON RESIN PA66Zytel® FG133F1 NC010(PRELIMINARY)
CHARACTERISTICS
Regional availability
North America
Europe
Asia Pacific
South and Central America
Near East/Africa
Global
Processing
Injection Moulding
Delivery form
Pellets
Additives
Release agent
PRODUCT TEXT
Zytel® FG133F1 NC010 is unreinforced, nucleated polyamide 66. It has been developed for consideration into applications such as parts for the food industry.
FOOD CONTACT
This product is manufactured according to Good Manufacturing Practice (GMP) principles and generally accepted in food contact applications in Europe and the USA when meeting applicable use conditions. For details, individual compliance statements are available from your DuPont representative.
DRY/COND.
TEST NORM
Resin Identification
PA66
ISO 1043
Part Marking Code
>PA66<
ISO 11469
ISO designation
ISO 16396-PA66,,M1G1NR,S14-040
-
DRY/COND.
UNIT
TEST NORM
Viscosity number
143/*
cm3/g
ISO 307, 1157, 1628
Moulding shrinkage, parallel
0.8/-
%
ISO 294-4, 2577
Moulding shrinkage, normal
1.0/-
%
ISO 294-4, 2577
DRY/COND.
UNIT
TEST NORM
Tensile Modulus
3800/-
MPa
ISO 527-1/-2
Yield stress
94/-
MPa
ISO 527-1/-2
Yield strain
6/-
%
ISO 527-1/-2
Nominal strain at break
14/-
%
ISO 527-1/-2
Charpy notched impact strength, 23°C
3/-
kJ/m2
ISO 179/1eA
Poisson's ratio
0.36/-
-
-
DRY/COND.
UNIT
TEST NORM
Melting temperature, 10°C/min
262/*
°C
ISO 11357-1/-3
Temp. of deflection under load, 1.8 MPa
78/*
°C
ISO 75-1/-2
DRY/COND.
UNIT
TEST NORM
FMVSS Class
B
-
ISO 3795 (FMVSS 302)
Burning rate, Thickness 1 mm
<80
mm/min
ISO 3795 (FMVSS 302)
DRY/COND.
UNIT
TEST NORM
Density
1140/-
kg/m3
ISO 1183
DRY/COND.
UNIT
Drying Recommended
yes
Drying Temperature
80
°C
Drying Time, Dehumidified Dryer
2 - 4
h
Processing Moisture Content
≤0.2
%
Melt Temperature Optimum
290
°C
Min. melt temperature
280
°C
Max. melt temperature
300
°C
Max. screw tangential speed
0.4
m/s
Mold Temperature Optimum
70
°C
Min. mould temperature
50
°C
Max. mould temperature
90
°C
Hold pressure range
50 - 100
MPa
Hold pressure time
4
s/mm
Ejection temperature
190
°C
DRY/COND.
UNIT
Drying Temperature
≤80
°C
Drying Time, Dehumidified Dryer
3 - 4
h
Processing Moisture Content
≤0.06
%
Melt Temperature Optimum
240
°C
Melt Temperature Range
235 - 250
°C
PA66产品型号
杜邦PA66 101F 通用级
杜邦PA66 101L 通用级
杜邦PA66 FR15 纯树脂 防火V0
杜邦PA66 FR7025V0 纯树脂 防火V0
杜邦PA66 FR50 玻璃纤维增强25% 防火V0
杜邦PA66 408HS 热稳定
杜邦PA66 103HSL 热稳定
杜邦PA66 8018HS 玻璃纤维增强14% 超韧 耐热
杜邦PA66 8018 玻璃纤维增强14% 超韧
杜邦PA66 408L 超高抗冲击
杜邦PA66 80G33L 玻璃纤维增强33% 超韧 耐冲
杜邦PA66 FE5171 玻璃纤维增强33% FDA
杜邦PA66 ST801 超韧耐寒耐冲
杜邦PA66 132F 35L 纯树脂高抗冲
杜邦PA66 70G33L 玻璃纤维增强33% 高强度 高刚性
杜邦PA66 70G25L 玻璃纤维增强25% 高强度 高刚性
杜邦PA66 70G13L 玻璃纤维增强13%
杜邦PA66 70G50L 玻璃纤维增强50% 高强度 高刚性
杜邦PA66 70G43L 玻璃纤维增强43% 高强度 高刚性
杜邦PA66 71G33L 玻璃纤维增强33% 耐冲击
杜邦PA66 74G33J 玻璃纤维增强30% 高强度 高刚性 表面改良
杜邦PA66 3426 高透明
巴斯夫PA66 A3K 易流动 快速注射级 用于高应力工程制件
巴斯夫PA66 A3EG3 玻璃纤维增强15% 用于中等刚性的机械部件和护罩
巴斯夫PA66 A3EG6 玻璃纤维增强30% 用于需要高刚性和尺寸稳定性的机械部件护罩
巴斯夫PA66 A3EG7 玻璃纤维增强35% 用于需要高刚性和尺寸稳定性的机械部件护罩
巴斯夫PA66 A3EG10 玻璃纤维增强50% 用于需要高钢性的工业部件
巴斯夫PA66 A3X2G5 玻璃纤维增强25% 红磷无卤阻燃V0
巴斯夫PA66 A3X2G7 玻璃纤维增强35% 红磷无卤阻燃V0
巴斯夫PA66 C3U 高韧性 无卤无磷阻燃V0 用于电绝缘部件
巴斯夫PA66 A3Z 超韧抗冲击 适用于具有良好耐低温冲击，耐热变形的原件和外壳。
罗地亚PA66 A205F 高流动
罗地亚PA66 B50H1 无卤阻燃V0
罗地亚PA66 A246M 超韧耐寒
首诺PA66 21SPC V2 通用
旭化成PA66 1300S 用于接插件 线圈轴心 电缆材料
东丽PA66 CM3001 一般级
东丽PA66 CM3004-V0 无卤防火VO
东丽PA66 CM3004G-15 玻璃纤维增强15% 防火V0
东丽PA66 CM3004G-30 玻璃纤维增强30% 防火V0
东丽PA66 CM3006 一般级
东丽PA66 CM3006G-15 玻璃纤维增强15%
东丽PA66 CM3006G-30 玻璃纤维增强30%