德国巴斯夫PA66 A3Z 热稳定 耐热老化 用于外壳组件：
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density
|
1.06
|
--
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.70
|
--
|
g/cm3
|
|
|
Melt Volume-Flow Rate (MVR) (275°C/10.0 kg)
|
21
|
--
|
cm3/10min
|
ISO 1133 |
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
6.7 to 7.7
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
2.0 to 2.6
|
--
|
%
|
|
|
Mold Shrinkage - constrained 3
|
0.85
|
--
|
%
|
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus
|
1900
|
850
|
MPa
|
ISO 527-1 |
|
Tensile Stress (Yield)
|
48.0
|
40.0
|
MPa
|
ISO 527-2/50 |
|
Tensile Strain (Yield)
|
5.0
|
18
|
%
|
ISO 527-2/50 |
|
Nominal Tensile Strain at Break
|
45
|
> 50
|
%
|
ISO 527-2/50 |
|
Tensile Creep Modulus 4 (1000 hr)
|
--
|
450
|
MPa
|
ISO 899-1 |
|
Flexural Modulus
|
1750
|
--
|
MPa
|
ISO 178 |
|
Flexural Stress
|
64.0
|
--
|
MPa
|
ISO 178 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
31
|
--
|
kJ/m2
|
|
|
23°C
|
90 kJ/m2
|
No Break
|
|