德国巴斯夫PA66 A3EG10物性表：
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
|||
|
Agency Ratings
|
|
|||
|
RoHS Compliance
|
|
|||
|
Forms
|
|
|||
|
Processing Method
|
|
|||
|
Multi-Point Data
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density
|
1.56
|
--
|
g/cm3
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0.70
|
--
|
g/cm3
|
|
|
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)
|
8.0
|
--
|
cm3/10min
|
ISO 1133 |
|
Molding Shrinkage
|
ISO 294-4 | |||
|
Across Flow
|
0.82
|
--
|
%
|
|
|
Flow
|
0.33
|
--
|
%
|
|
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
3.7 to 4.3
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
1.0 to 1.4
|
--
|
%
|
|
|
Viscosity Number (96% H2SO4 (Sulphuric Acid))
|
130
|
--
|
cm3/g
|
ISO 307 |
|
Mold Shrinkage - constrained 3
|
0.45
|
--
|
%
|
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus
|
16800
|
12500
|
MPa
|
ISO 527-1 |
|
Tensile Stress (Break)
|
240
|
180
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break)
|
2.5
|
3.5
|
%
|
ISO 527-2 |
|
Tensile Creep Modulus 4 (1000 hr)
|
--
|
7800
|
MPa
|
ISO 899-1 |
|
Flexural Modulus
|
15000
|
13500
|
MPa
|
ISO 178 |
|
Flexural Stress
|
360
|
300
|
MPa
|
ISO 178 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179/1eA | |||
|
-30°C
|
13
|
--
|
kJ/m2
|
|
|
23°C
|
18
|
25
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179/1eU | |||
|
-30°C
|
90
|
--
|
kJ/m2
|
|
|
23°C
|
95
|
100
|
kJ/m2
|
|
|
Notched Izod Impact Strength (23°C)
|
13
|
15
|
kJ/m2
|
ISO 180/A |
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
||||
|
0.45 MPa, Unannealed
|
260
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
250
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature
|
260
|
--
|
°C
|
ISO 11357-3 |
|
CLTE
|
ISO 11359-2 | |||
|
Flow : 23 to 80°C
|
5.0E-6 to 2.0E-5
|
--
|
cm/cm/°C
|
|
|
Transverse : 23 to 80°C
|
5.0E-5 to 6.0E-5
|
--
|
cm/cm/°C
|
|
|
Specific Heat
|
1300
|
--
|
J/kg/°C
|
|
|
Thermal Conductivity
|
0.37
|
--
|
W/m/K
|
DIN 52612 |
|
Maximum Service Temperature - short cycle operation
|
240
|
--
|
°C
|
|
|
Temperature Index - at 50% loss of tensile strength
|
IEC 60216 | |||
|
-- 5
|
165
|
--
|
°C
|
|
|
-- 6
|
135
|
--
|
°C
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Surface Resistivity
|
--
|
1.0E+10
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
1.0E+15
|
1.0E+12
|
ohms·cm
|
IEC 60093 |
|
Relative Permittivity (1 MHz)
|
3.80
|
6.60
|
|
IEC 60250 |
|
Dissipation Factor (1 MHz)
|
0.015
|
0.17
|
|
IEC 60250 |
|
Comparative Tracking Index (Solution A)
|
550
|
--
|
V
|
IEC 60112 |