PA66 A3HG5德国巴斯夫原料粒子：
PA66 A3HG6 HR德国巴斯夫原料包装图片：
PA66 A3HG6 HR德国巴斯夫原料物性表：
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density
|
1.37
|
--
|
g/cm3
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)
|
25
|
--
|
cm3/10min
|
ISO 1133 |
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
5.5
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
1.7
|
--
|
%
|
|
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
225
|
175
|
MPa
|
ISO 2039-1 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
10000
|
6800
|
MPa
|
ISO 527-1 |
|
Tensile Stress
|
ISO 527-2 | |||
|
Break, -40°C
|
240
|
231
|
MPa
|
|
|
Break, 23°C
|
190
|
120
|
MPa
|
|
|
Tensile Strain
|
ISO 527-2 | |||
|
Break, -40°C
|
3.1
|
3.0
|
%
|
|
|
Break, 23°C
|
3.2
|
5.4
|
%
|
|
|
Flexural Modulus (23°C)
|
8700
|
5800
|
MPa
|
ISO 178 |
|
Flexural Stress (23°C)
|
275
|
200
|
MPa
|
ISO 178 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179 | |||
|
-30°C
|
9.0
|
--
|
kJ/m2
|
|
|
23°C
|
11
|
16
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179 | |||
|
-30°C
|
65
|
--
|
kJ/m2
|
|
|
23°C
|
80
|
90
|
kJ/m2
|
|
|
Notched Izod Impact Strength
|
ISO 180 | |||
|
-30°C
|
9.0
|
--
|
kJ/m2
|
|
|
23°C
|
13
|
20
|
kJ/m2
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
||||
|
0.45 MPa, Unannealed
|
250
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
250
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature (DSC)
|
260
|
--
|
°C
|
ISO 3146 |