德国巴斯夫pa66 A3EG6 FC 物性表：
Physical
Dry
Conditioned
Unit
Test Method
Density
1.36
--
g/cm3
ISO 1183
Apparent (Bulk) Density
0.70
--
g/cm3
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)
40
--
cm3/10min
ISO 1133
Water Absorption
ISO 62
Saturation, 23°C
5.2 to 5.8
--
%
Equilibrium, 23°C, 50% RH
1.5 to 1.9
--
%
Viscosity Number (96% H2SO4 (Sulphuric Acid))
145
--
cm3/g
ISO 307
Mold Shrinkage - constrained 3
0.55
--
%
Mechanical
Dry
Conditioned
Unit
Test Method
Tensile Modulus
10000
7200
MPa
ISO 527-1
Tensile Stress (Break)
190
130
MPa
ISO 527-2
Tensile Strain (Break)
3.0
5.0
%
ISO 527-2
Tensile Creep Modulus 4 (1000 hr)
--
5300
MPa
ISO 899-1
Flexural Modulus
8600
6500
MPa
ISO 178
Flexural Stress
280
210
MPa
ISO 178
Impact
Dry
Conditioned
Unit
Test Method
Charpy Notched Impact Strength
ISO 179/1eA
-30°C
11
--
kJ/m2
23°C
13
22
kJ/m2
Charpy Unnotched Impact Strength
ISO 179/1eU
-30°C
70
--
kJ/m2
23°C
85
100
kJ/m2
Notched Izod Impact Strength (23°C)
12
16
kJ/m2
ISO 180/A
Thermal
Dry
Conditioned
Unit
Test Method
Deflection Temperature Under Load
0.45 MPa, Unannealed
250
--
°C
ISO 75-2/B
1.8 MPa, Unannealed
250
--
°C
ISO 75-2/A
Melting Temperature
260
--
°C
ISO 11357-3
Specific Heat
1500
--
J/kg/°C
Thermal Conductivity
0.35
--
W/m/K
DIN 52612
Maximum Service Temperature - short cycle operation
240
--
°C
Temperature Index - at 50% loss of tensile strength
IEC 60216