德国巴斯夫PA66 A3WGM53概述：
Ultramid® A3WGM53 BK20560
德国巴斯夫PA66 A3WGM53物性表：
|
Features
|
|
|||
|
Uses
|
|
|||
|
Agency Ratings
|
|
|||
|
RoHS Compliance
|
|
|||
|
Appearance
|
|
|||
|
Forms
|
|
|||
|
Processing Method
|
|
| Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Density
|
1.48
|
--
|
g/cm3
|
ISO 1183 |
|
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)
|
30
|
--
|
cm3/10min
|
ISO 1133 |
|
Water Absorption
|
ISO 62 | |||
|
Saturation, 23°C
|
5.1
|
--
|
%
|
|
|
Equilibrium, 23°C, 50% RH
|
1.4
|
--
|
%
|
|
| Hardness |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Ball Indentation Hardness
|
230
|
90.0
|
MPa
|
ISO 2039-1 |
| Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
12100
|
6100
|
MPa
|
ISO 527-1 |
|
Tensile Stress (Break, 23°C)
|
160
|
80.0
|
MPa
|
ISO 527-2 |
|
Tensile Strain (Break, 23°C)
|
2.3
|
6.0
|
%
|
ISO 527-2 |
|
Flexural Modulus (23°C)
|
10100
|
5500
|
MPa
|
ISO 178 |
|
Flexural Stress (23°C)
|
225
|
125
|
MPa
|
ISO 178 |
| Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179 | |||
|
-30°C
|
6.7
|
--
|
kJ/m2
|
|
|
23°C
|
8.0
|
16
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
ISO 179 | |||
|
-30°C
|
50
|
--
|
kJ/m2
|
|
|
23°C
|
55
|
62
|
kJ/m2
|
|
|
Notched Izod Impact Strength
|
ISO 180 | |||
|
-30°C
|
7.5
|
--
|
kJ/m2
|
|
|
23°C
|
9.5
|
16
|
kJ/m2
|
| Thermal |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
||||
|
0.45 MPa, Unannealed
|
250
|
--
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
225
|
--
|
°C
|
ISO 75-2/A |
|
Melting Temperature (DSC)
|
260
|
--
|
°C
|
ISO 3146 |
|
CLTE - Flow
|
1.5E-5
|
--
|
cm/cm/°C
|
| Electrical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
|
Volume Resistivity
|
1.0E+15
|
1.0E+12
|
ohms·cm
|
IEC 60093 |
|
Dielectric Constant (1 MHz)
|
4.00
|
--
|
|
IEC 60250 |