LCP 产品简介：
LCP塑胶原料颗粒展示
物性表：
| Search for UL Yellow Card |
|
| Availability |
Asia Pacific
Europe
Latin America
North America
|
| Filler / Reinforcement |
Glass Fiber, 40% Filler by Weight
|
| Features |
High Heat Resistance
Low CLTE
|
| Uses |
Automotive Applications
Bobbins/Spools
Business Equipment
Connectors
Electrical/Electronic Applications
Printer Parts
Switches
|
| UL File Number |
E249884
E54705
|
| Appearance |
Black
Off-White
Opaque
|
| Forms |
Pellets
|
| Processing Method |
Injection Molding
|
| Part Marking Code (ISO 11469) |
>LCP-GF40<
|
| PHYSICAL |
Nominal Value
|
Unit
|
Test Method
|
| Density / Specific Gravity |
1.69
|
g/cm3
|
ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.00 mm |
0.050
|
%
|
|
| Across Flow : 3.00 mm |
0.81
|
%
|
|
| Water Absorption (24 hr, 23°C) |
0.020
|
%
|
ASTM D570 |
| MECHANICAL |
Nominal Value
|
Unit
|
Test Method
|
| Tensile Modulus |
17000
|
MPa
|
ISO 527-1 |
| Tensile Strength | |||
| -- |
123
|
MPa
|
ASTM D638 |
| -- |
108
|
MPa
|
ISO 527-2 |
| Tensile Elongation | |||
| Break |
3.7
|
%
|
ASTM D638 |
| Break |
0.90
|
%
|
ISO 527-2 |
| Flexural Modulus | |||
| -- |
13400
|
MPa
|
ASTM D790 |
| -- |
17000
|
MPa
|
ISO 178 |
| Flexural Strength | |||
| -- |
127
|
MPa
|
ASTM D790 |
| -- |
168
|
MPa
|
ISO 178 |
| IMPACT |
Nominal Value
|
Unit
|
Test Method
|
| Charpy Unnotched Impact Strength |
36
|
kJ/m2
|
ISO 179/1eU |
| Unnotched Izod Impact | |||
| -- |
320
|
J/m
|
ASTM D256 |
| -- |
24
|
kJ/m2
|
ISO 180/1U |
| HARDNESS |
Nominal Value
|
Unit
|
Test Method
|
| Rockwell Hardness (R-Scale) |
100
|
|
ASTM D785 |
| THERMAL |
Nominal Value
|
Unit
|
Test Method
|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed |
339
|
°C
|
ASTM D648 |
| 1.8 MPa, Unannealed |
326
|
°C
|
ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow : 50 to 150°C |
2.0E-6
|
cm/cm/°C
|
|
| Transverse : 50 to 150°C |
6.0E-5
|
cm/cm/°C
|
| ELECTRICAL |
Nominal Value
|
Unit
|
Test Method
|
| Volume Resistivity |
1.0E+13
|
ohms·cm
|
IEC 60093 |
| Electric Strength (1.00 mm) |
37
|
kV/mm
|
IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 1 MHz |
4.20
|
|
|
| 1.00 GHz |
3.70
|
|
|
| 10.0 GHz |
3.80
|
|
|
| Dissipation Factor | IEC 60250 | ||
| 1 MHz |
0.031
|
|
|
| 1.00 GHz |
5.0E-3
|
|
|
| 10.0 GHz |
5.0E-3
|
|
|
| Arc Resistance |
128
|
sec
|
ASTM D495 |
| Comparative Tracking Index |
185
|
V
|
IEC 60112 |