PA66 CM3006G-15日本东丽尼龙物性表
| Filler / Reinforcement |
Glass Fiber, 15% Filler by Weight
|
| Additive |
Heat Stabilizer
|
| Features |
Chemical Resistant
High Heat Resistance
High Strength
|
| Uses |
Automotive Applications
Automotive Electronics
Electrical/Electronic Applications
White Goods & Small Appliances
|
| Processing Method |
Injection Molding
|
| ISO Designation |
>PA66-GF15<
|
| PHYSICAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Density (23°C) |
1.26
|
--
|
g/cm3
|
ISO 1183 |
| Spiral Flow 3 |
52.0
|
--
|
cm
|
Internal Method |
| Molding Shrinkage 4 | Internal Method | |||
| Across Flow : 3.00 mm |
1.0 to 1.4
|
--
|
%
|
|
| Flow : 3.00 mm |
0.70 to 1.0
|
--
|
%
|
|
| Water Absorption 5 | ISO 62 | |||
| 24 hr, 23°C |
1.0
|
--
|
%
|
|
| Saturation, 23°C |
7.2
|
--
|
%
|
| MECHANICAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Tensile Stress | ISO 527-2 | |||
| -40°C |
155
|
145
|
MPa
|
|
| 23°C |
110
|
90.0
|
MPa
|
|
| 80°C |
65.0
|
50.0
|
MPa
|
|
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C |
2.0
|
--
|
%
|
|
| Break, 23°C |
2.0
|
4.5
|
%
|
|
| Break, 80°C |
7.5
|
--
|
%
|
|
| Flexural Modulus | ISO 178 | |||
| -40°C |
6600
|
6300
|
MPa
|
|
| 23°C |
5800
|
3700
|
MPa
|
|
| 80°C |
2800
|
2200
|
MPa
|
|
| Flexural Stress | ISO 178 | |||
| -40°C |
225
|
190
|
MPa
|
|
| 23°C |
180
|
135
|
MPa
|
|
| 80°C |
115
|
85.0
|
MPa
|
|
| Shear Strength (23°C) |
80.0
|
--
|
MPa
|
ASTM D732 |
| IMPACT |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Charpy Notched Impact Strength (23°C) |
6.0
|
--
|
kJ/m2
|
ISO 179 |
| Charpy Unnotched Impact Strength (23°C) |
30
|
--
|
kJ/m2
|
ISO 179 |
| HARDNESS |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Rockwell Hardness | ISO 2039-2 | |||
| M-Scale, 23°C |
95
|
--
|
|
|
| R-Scale, 23°C |
120
|
--
|
|