日本三井PA6T
物性表
MECHANICAL
Dry
Conditioned
Unit
Test Method
Tensile Strength
170
140
MPa
ASTM D638
Tensile Elongation (Break)
3.0
3.0
%
ASTM D638
Flexural Modulus
10000
7000
MPa
ASTM D790
Flexural Strength
260
220
MPa
ASTM D790
IMPACT
Dry
Conditioned
Unit
Test Method
Notched Izod Impact
80
90
J/m
ASTM D256
HARDNESS
Dry
Conditioned
Unit
Test Method
Rockwell Hardness (M-Scale)
110
--
ASTM D785
THERMAL
Dry
Conditioned
Unit
Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)
300
--
°C
ASTM D648
Glass Transition Temperature
85.0
--
°C
DSC
Melting Temperature
310
--
°C
CLTE
ASTM D696
Flow
2.4E-5
--
cm/cm/°C
Transverse
5.0E-5
--
cm/cm/°C
ELECTRICAL
Dry
Conditioned
Unit
Test Method
Volume Resistivity
1.0E+16
--
ohms·cm
ASTM D257
Dielectric Strength
28
--
kV/mm
ASTM D149
Dielectric Constant (1 MHz)
4.50
--
ASTM D150
Dissipation Factor (1 MHz)
0.018
--
ASTM D150
FLAMMABILITY
Dry
Conditioned
Unit
Test Method
Flame Rating
HB
--
UL 94
INJECTION
Dry
Unit
Drying Temperature
110
°C
Drying Time
2.0 to 6.0
hr
Hopper Temperature
50 to 90
°C
Rear Temperature
300 to 325
°C
Middle Temperature
315 to 335
°C
Front Temperature
320 to 335
°C
Nozzle Temperature
315 to 335
°C
Mold Temperature
90 to 140
°C
Injection Rate
Moderate
Screw Speed
150
rpm
INJECTION NOTES
Injection Pressure: Medium Pressure