美国杜邦PA66Zytel FR50 NC01025% Polyamide 66物性表
| Filler / Reinforcement | Glass Fiber, 25% Filler by Weight |
| Additive | Flame Retardant |
| Features | Flame Retardant |
| Forms | Pellets |
| Processing Method | Injection Molding |
| Multi-Point Data | Isothermal Stress vs. Strain (ISO 11403) Secant Modulus vs. Strain (ISO 11403) |
| ISO Designation | ISO 16396-PA66.GF25 FR(17).M1F1GNR.S14-100 |
| Part Marking Code (ISO 11469) | >PA66-GF25 FR(17)< |
| Resin ID (ISO 1043) | PA66-GF25 FR(17) |
| Physical | ||||
| Density | 1.57 | -- | g/cm3 | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 24 hr, 73°F | 0.60 | -- | % | |
| Equilibrium, 73°F, 0.0787 in, 50% RH | 1.3 | -- | % | |
| Viscosity Number | 150 | -- | cm3/g | ISO 307, 1628 |
| Mechanical | ||||
| Tensile Modulus | 1.45E+6 | 1.16E+6 | psi | ISO 527-1 |
| Tensile Stress (Break) | 24700 | 17400 | psi | ISO 527-2/5 |
| Tensile Strain (Break) | 2.6 | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | 1.38E+6 | 1.09E+6 | psi | ISO 178 |
| Impact | ||||
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°F | 5.7 | 4.8 | ft·lb/in2 | |
| -22°F | 5.7 | 5.2 | ft·lb/in2 | |
| 73°F | 5.7 | 6.2 | ft·lb/in2 | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°F | 24 | -- | ft·lb/in2 | |
| -22°F | 24 | -- | ft·lb/in2 | |
| 73°F | 29 | -- | ft·lb/in2 |
| Thermal | ||||
| Deflection Temperature Under Load (264 psi, Unannealed) | 464 | -- | °F | ISO 75-2/A |
| Glass Transition Temperature 4 | 176 | 68.0 | °F | ISO 11357-3 |
| Melting Temperature 4 | 504 | -- | °F | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : -40 to 73°F | 1.1E-5 | -- | in/in/°F | |
| Flow : 131 to 320°F | 1.2E-5 | -- | in/in/°F | |
| Transverse : -40 to 73°F | 3.1E-5 | -- | in/in/°F | |
| Transverse : 131 to 320°F | 6.1E-5 | -- | in/in/°F | |
| RTI Elec | UL 746B | |||
| 0.030 in | 266 | -- | °F | |
| 0.06 in | 266 | -- | °F | |
| 0.12 in | 266 | -- | °F | |
| RTI Imp | UL 746B | |||
| 0.030 in | 221 | -- | °F | |
| 0.06 in | 239 | -- | °F | |
| 0.12 in | 239 | -- | °F | |
| RTI Str | UL 746B | |||
| 0.030 in | 221 | -- | °F | |
| 0.06 in | 239 | -- | °F | |
| 0.12 in | 248 | -- | °F |
| Injection | Dry | Unit | |
| Drying Temperature | 176 | °F | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 536 to 572 | °F | |
| Melt Temperature, Optimum | 554 | °F | |
| Mold Temperature | 158 to 248 | °F | |
| Mold Temperature, Optimum | 212 | °F | |
| Holding Pressure | 7250 to 14500 | psi | |
| Screw Tangential Speed | < 472 | in/min | |
| Drying Recommended | yes | | |
| Hold Pressure Time | 3.00 | s/mm |